Production of fiberboards from shives collected after continuous fiber mechanical extraction from oleaginous flax
Fabrication de panneaux agglomérés de fibres à partir des anas collectés lors de l’extraction mécanique des fibres libériennes de la paille de lin oléagineux
Résumé
In this study, fiberboards were produced from shives collected after continuous fiber mechanical extraction from oleaginous flax straw. Fiberboards were produced through thermo-pressing, and their mechanical and thermo-mechanical properties were studied, as well as their water resistance. The influence of one pretreatment for shives and lignin addition was investigated on the different properties. Boards obtained were all cohesive hardboards. The optimal board was obtained from fibers extruded from shives and without addition of any supplementary lignin amount. Looking at its characteristics and standard NF EN 312, the latter perfectly complied with the requirements for type P1 boards, i.e. boards for general uses in dry conditions.
Dans cette étude, des panneaux agglomérés de fibres ont été produits à partir d’anas collectés après extraction mécanique des fibres libériennes de paille de lin oléagineux. Les panneaux ont été mis en oeuvre par thermopressage. Leurs propriétés mécaniques et thermo-mécaniques ont été étudiées ainsi que leur comportement vis-à-vis de l’eau. L’influence d’un prétraitement thermo-mécanique des anas bruts à l’aide d’une extrudeuse bi-vis a été étudiée ainsi que l’ajout de lignine exogène. Tous les panneaux mis en oeuvre possèdent une tenue suffisante pour être manipulés à la main. Le panneau ayant obtenu les propriétés optimales a été obtenu à partir des anas extrudés et sans ajout supplémentaire de lignine. Au regard de ses caractéristiques et du standard NF EN 312, ce dernier remplit complètement les critères d’un panneau aggloméré de type P1 (panneau d’usage général utilisé en milieu sec).
| Origine | Fichiers éditeurs autorisés sur une archive ouverte |
|---|